[RTP Company]

Product Data Sheet &
General Processing Conditions


PermaStat® 600
Acrylonitrile Butadiene Styrene (ABS)
ESD Protection
Permanently Anti-static



PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS

PERMANENCE
English SI Metric ASTM
TEST
 
Specific Gravity1.06 1.06  D 792
Molding Shrinkage 
    1/8 in (3.2 mm) section0.0060 - 0.0080 in/in 0.60 - 0.80 %  D 955

MECHANICAL
 
Impact Strength, Izod 
    notched 1/8 in (3.2 mm) section4.0 ft-lbs/in 214 J/m  D 256
    unnotched 1/8 in (3.2 mm) sectionNo Break No Break  D 4812
Tensile Strength6000 psi 41 MPa  D 638
Tensile Elongation> 10.0 % > 10.0 %  D 638
Tensile Modulus0.28 x 10^6 psi 1931 MPa  D 638
Flexural Strength10000 psi 69 MPa  D 790
Flexural Modulus0.31 x 10^6 psi 2137 MPa  D 790

ELECTRICAL
 
Volume Resistivity1E9 - 9.9E10 ohm.cm 1E9 - 9.9E10 ohm.cm  D 257
Surface Resistivity1E10 - 9.9E11 ohm/sq 1E10 - 9.9E11 ohm/sq  D 257
ESD STM11.11
Surface Resistance1E9 - 9.9E10 ohm 1E9 - 9.9E10 ohm  ESD STM11.11
Static Decay 
    MIL-PRF-81705D, 5kV to 50 V, 12% RH< 2.00 s < 2.00 s  FTMS101C
4046.1

THERMAL
 
Deflection Temperature 
    @ 264 psi (1820 kPa)170 °F 77 °C  D 648
 
PROPERTY NOTES
 
Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.

GENERAL PROCESSING FOR INJECTION MOLDING
 English SI Metric  
 
Injection Pressure10000 - 15000 psi 69 - 103 MPa  
Melt Temperature390 - 460 °F 199 - 238 °C  
Mold Temperature120 - 200 °F 49 - 93 °C  
Drying2 hrs @ 180 °F 2 hrs @ 82 °C  
Moisture Content0.10 % 0.10 %  
Dew Point0 °F -18 °C  

PROCESSING NOTES
 
Do not exceed 520 °F (270 °C) melt temperature.
Desiccant Type Dryer Required.

18 May 2010 GJF

This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.

Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.

No information supplied by RTP Company constitutes a warranty regarding product performance or use. Any information regarding performance or use is only offered as suggestion for investigation for use, based upon RTP Company or other customer experience. RTP Company makes no warranties, expressed or implied, concerning the suitability or fitness of any of its products for any particular purpose. It is the responsibility of the customer to determine that the product is safe, lawful and technically suitable for the intended use. The disclosure of information herein is not a license to operate under, or a recommendation to infringe any patents.

RTP COMPANY • 580 EAST FRONT STREET • WINONA, MN 55987 • 507-454-6900