PermaStat® 100
Polypropylene (PP)
Permanently Anti-static
ESD Protection



PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS

PERMANENCE
English SI Metric ASTM
TEST
 
Specific Gravity0.92 0.92  D 792
Molding Shrinkage 
    1/8 in (3.2 mm) section0.0100 - 0.0150 in/in 1.00 - 1.50 %  D 955

MECHANICAL
 
Impact Strength, Izod 
    notched 1/8 in (3.2 mm) section1.2 ft-lbs/in 64 J/m  D 256
    unnotched 1/8 in (3.2 mm) sectionNo Break No Break  D 4812
Tensile Strength4000 psi 28 MPa  D 638
Tensile Elongation> 10.0 % > 10.0 %  D 638
Tensile Modulus0.25 x 10^6 psi 1724 MPa  D 638
Flexural Strength6000 psi 41 MPa  D 790
Flexural Modulus0.20 x 10^6 psi 1379 MPa  D 790

ELECTRICAL
 
Volume Resistivity1.0e9 - 9.9e10 ohm.cm 1.0e9 - 9.9e10 ohm.cm  D 257
Surface Resistivity1.0e10 - 9.9e11 ohm/sq 1.0e10 - 9.9e11 ohm/sq  D 257
ESD STM11.11
Surface Resistance1.0e9 - 9.9e10 ohm 1.0e9 - 9.9e10 ohm  ESD STM11.11
Static Decay 
    MIL-PRF-81705D, 5kV to 50 V, 12% RH< 2.00 s < 2.00 s  FTMS101C
4046.1
 
PROPERTY NOTES
 
Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.

GENERAL PROCESSING FOR INJECTION MOLDING
 English SI Metric  
 
Injection Pressure7000 - 11000 psi 48 - 76 MPa  
Melt Temperature340 - 400 °F 171 - 204 °C  
Mold Temperature90 - 150 °F 32 - 66 °C  
Drying2 hrs @ 175 °F 2 hrs @ 79 °C  
Moisture Content0.10 % 0.10 %  

PROCESSING NOTES
 
Do not exceed 520 °F (270 °C) melt temperature.

16 Dec 2004 LCR

This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.

Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.

No information supplied by RTP Company constitutes a warranty regarding product performance or use. Any information regarding performance or use is only offered as suggestion for investigation for use, based upon RTP Company or other customer experience. RTP Company makes no warranties, expressed or implied, concerning the suitability or fitness of any of its products for any particular purpose. It is the responsibility of the customer to determine that the product is safe, lawful and technically suitable for the intended use. The disclosure of information herein is not a license to operate under, or a recommendation to infringe any patents.