[RTP Company]

Product Data Sheet &
General Processing Conditions

RTP 2099 X 134682
Polycarbonate/PBT Alloy
Permanently Static Dissipative
ESD Protection
Impact Modified
UV Stabilized
UL94 Tested

This compound has been formulated to meet the static dissipative requirements of the ATEX Directive.


English SI Metric ASTM
Specific Gravity1.17 1.17  D 792
Melt Flow Rate 
    @ 230 °C, / 3.8 kg5.00 - 8.00 g/10 min 5.00 - 8.00 g/10 min  D 1238
Molding Shrinkage 
    1/8 in (3.2 mm) section0.0060 - 0.0080 in/in 0.60 - 0.80 %  D 955

Impact Strength, Izod 
    notched 1/8 in (3.2 mm) section15.0 ft-lbs/in 801 J/m  D 256
    unnotched 1/8 in (3.2 mm) sectionNo Break No Break  D 4812
Tensile Strength6200 psi 43 MPa  D 638
Tensile Elongation> 10.0 % > 10.0 %  D 638
Tensile Modulus0.23 x 10^6 psi 1586 MPa  D 638
Flexural Strength10000 psi 69 MPa  D 790
Flexural Modulus0.26 x 10^6 psi 1793 MPa  D 790

Surface Resistance*< 1E9 ohm < 1E9 ohm  IEC 60079:0
Static Decay 
    MIL-PRF-81705D, 5kV to 50 V, 12% RH< 0.50 s < 0.50 s  FTMS101C

Ignition Resistance* 
    FlammabilityHB @ 1/32 in  HB @ 0.8 mm  UL94
Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.
*ATEX Directive mandates <1.0E+09 ohm surface resistance.
* This rating is not intended to reflect hazards of this or any other material under actual fire conditions.

 English SI Metric  
Injection Pressure10000 - 15000 psi 69 - 103 MPa  
Melt Temperature410 - 480 °F 210 - 249 °C  
Mold Temperature150 - 230 °F 66 - 110 °C  
Drying4 hrs @ 180 °F 4 hrs @ 82 °C  
Moisture Content< 0.02 % < 0.02 %  

Do not exceed 520 F (270 C) melt temperature.
Desiccant Type Dryer Required.
26 Jan 2017 RJS

This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.

Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.

No information supplied by RTP Company constitutes a warranty regarding product performance or use. Any information regarding performance or use is only offered as suggestion for investigation for use, based upon RTP Company or other customer experience. RTP Company makes no warranties, expressed or implied, concerning the suitability or fitness of any of its products for any particular purpose. It is the responsibility of the customer to determine that the product is safe, lawful and technically suitable for the intended use. The disclosure of information herein is not a license to operate under, or a recommendation to infringe any patents.

RTP COMPANY • 580 EAST FRONT STREET • WINONA, MN 55987 • 507-454-6900