Polabond® 6003-45A
Speciality Thermoplastic Elastomer
PC/PMMA, PC/PBT bondable


English SI Metric ASTM
Specific Gravity0.96 0.96  D 792

Tensile Strength 
    Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min)780 psi 5 MPa  D 412
Tensile Elongation 
    Break, Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min)630.0 % 630.0 %  D 412
Tensile Stress 
    Die C 0.125 in, 20 in/min (3.2 mm, 500 mm/min) 
    @ 100 %220.0 psi 1.5 MPa  D 412
Tear Strength, Die C140.0 pli 24.5 N/mm  D 624
Peel Strength *** 
    90 degrees, 20 in/min (500 mm/min) 
    PC/PMMA, Failure Type D24.0 pli 4.2 N/mm  RTP 55
    PC/PBT, Failure Type D20.0 pli 3.5 N/mm  RTP 55
Compression Set 
    22 h @ 23 °C (73 °F), Method B, Type 216 % 16 %  D 395
    22 h @ 70 °C (158 °F), Method B, Type 266 % 66 %  D 395
    Shore A, 10 s delay45 45  D 2240

Ignition Resistance* 
    Flammability**HB @ 1/16 in  HB @ 1.5 mm  D 635
Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.
* This rating is not intended to reflect hazards of this or any other material under actual fire conditions.
** Values per RTP Company testing.
*** Values per RTP Company testing. Failure types: R=overmold failure, D=interface failure, S=substrate failure.

 English SI Metric  
Melt Temperature380 - 460 °F 193 - 238 °C  
Mold Temperature70 - 120 °F 21 - 49 °C  
Drying2 - 4 hrs @ 180 °F 2 - 4 hrs @ 82 °C  
Moisture Content< 0.03 % < 0.03 %  
Dew Point0 °F -18 °C  

Desiccant Type Dryer Required.
8 Mar 2016 SAC

This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.

Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.

No information supplied by RTP Company constitutes a warranty regarding product performance or use. Any information regarding performance or use is only offered as suggestion for investigation for use, based upon RTP Company or other customer experience. RTP Company makes no warranties, expressed or implied, concerning the suitability or fitness of any of its products for any particular purpose. It is the responsibility of the customer to determine that the product is safe, lawful and technically suitable for the intended use. The disclosure of information herein is not a license to operate under, or a recommendation to infringe any patents.