Product Data Sheet &
General Processing Conditions


RTP 1405 N
Polyethersulfone (PES)
Glass Fiber
High Viscosity



PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS

PERMANENCE
English SI Metric ASTM
TEST
 
Primary Additive30 % 30 %  
Specific Gravity1.59 1.59  D 792
Molding Shrinkage 
    1/8 in (3.2 mm) section0.0020 in/in 0.20 %  D 955
Water Absorption, 24 hrs @ 23°C0.350 % 0.350 %  D 570

MECHANICAL
 
Impact Strength, Izod 
    notched 1/8 in (3.2 mm) section1.8 ft-lbs/in 96 J/m  D 256
    unnotched 1/8 in (3.2 mm) section14.0 ft-lbs/in 747 J/m  D 4812
Tensile Strength21500 psi 148 MPa  D 638
Tensile Elongation2.6 % 2.6 %  D 638
Tensile Modulus1.40 x 10^6 psi 9653 MPa  D 638
Flexural Strength30500 psi 210 MPa  D 790
Flexural Modulus1.30 x 10^6 psi 8964 MPa  D 790
Compressive Strength21000 psi 145 MPa  D 695
Hardness 
    Rockwell, R123 123  D 785

ELECTRICAL
 
Dielectric Strength, S/T, in oil370 VPM 14.6 kV/mm  D 149
Dielectric Constant, 1 MHz, Dry4.2 4.2  D 150
Dissipation Factor, 1 MHz, Dry0.0070 0.0070  D 150
Arc Resistance75 s 75 s  D 495
Volume Resistivity> 1E12 ohm.cm > 1E12 ohm.cm  D 257

THERMAL
 
Deflection Temperature 
    @ 264 psi (1820 kPa)420 °F 216 °C  D 648
    @ 66 psi (455 kPa)430 °F 221 °C  D 648
Ignition Resistance* 
    Flammability**V-0 @ 1/16 in  V-0 @ 1.5 mm  D 3801
Coefficient of Linear Thermal Expansion 
    Flow Direction1.5 x 10-5/°F 2.7 x 10-5/°C  E 831
Thermal Conductivity 
    Through-plane2.20 (BTU.in)/(hr.ft2.°F) 0.32 W/(m.K)  E 1530
 
PROPERTY NOTES
 
Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.
* This rating is not intended to reflect hazards of this or any other material under actual fire conditions.
** Values per RTP Company testing.

GENERAL PROCESSING FOR INJECTION MOLDING
 English SI Metric  
 
Injection Pressure10000 - 15000 psi 69 - 103 MPa  
Melt Temperature650 - 710 °F 343 - 377 °C  
Mold Temperature275 - 350 °F 135 - 177 °C  
Drying6 hrs @ 300 °F 6 hrs @ 149 °C  
Moisture Content0.04 % 0.04 %  
Dew Point-25 °F -32 °C  

PROCESSING NOTES
 
Desiccant Type Dryer Required.

22 Dec 2004 BMR

This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.

Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.

No information supplied by RTP Company constitutes a warranty regarding product performance or use. Any information regarding performance or use is only offered as suggestion for investigation for use, based upon RTP Company or other customer experience. RTP Company makes no warranties, expressed or implied, concerning the suitability or fitness of any of its products for any particular purpose. It is the responsibility of the customer to determine that the product is safe, lawful and technically suitable for the intended use. The disclosure of information herein is not a license to operate under, or a recommendation to infringe any patents.

RTP COMPANY • 580 EAST FRONT STREET • WINONA, MN 55987 • 507-454-6900